post-template-default,single,single-post,postid-1135,single-format-standard,ajax_fade,page_not_loaded,,qode_grid_1300,footer_responsive_adv,hide_top_bar_on_mobile_header,qode-content-sidebar-responsive,qode-theme-ver-15.0,qode-theme-bridge,disabled_footer_bottom,wpb-js-composer js-comp-ver-5.4.7,vc_responsive
 

Il progetto Opicem diventa una tesi di Laurea

Il progetto Opicem diventa una tesi di Laurea

Il progetto Opicem diventa una tesi di Laurea

Il progetto OPICEM diventa il protagonista della tesi di Laurea di Veronica Pasinato del Dipartimento di Geoscienze dell’Università degli Studi di Padova dal titolo “Characterization of metallurgical slags towards the formulation of alternative binders”.
Lo studio alla base del lavoro di tesi rappresenta un’opzione sostenibile all’urgente problema ambientale riguardante le enormi emissioni di CO₂ che provengono dalla calcinazione del calcare, uno dei materiali grezzi per produrre il cemento Portland.
Questo lavoro riguarda la caratterizzazione di tre tipi di scorie metallurgiche provenienti da stabilimenti italiani. Due di queste provengono da acciaierie che utilizzano un processo di fusione di arco elettrico, l’altra viene da una fonderia. L’intento è quello di sfruttare questi materiali di scarto per usarli come materiali cementizi aggiuntivi, incoraggiando l’uso di prodotti locali per produrre leganti alternativi.
Di seguito l’Abstract della Tesi.
The large CO₂ emissions which come from limestone calcination, one of the raw materials to produce Portland cement, pose an urgent global issue that requires industrially sustainable alternative options to replace this material.
This work is about the characterization of three types of metallurgical slags from Italian companies, two of them are from steel mills (with an EAF production process) and the other one from foundry process. We try to find if we can take advantage of these waste materials as supplementary cementitious materials, encouraging the use of local products to produce eco-sustainable binders.
The analyses done give us information about the elementary chemical composition, by the X-ray fluorescence, the mineralogic composition, by X-ray powder diffraction, and the particle size distribution by laser granulometry. Calorimetric data are important to assess the behaviour and the reactivity of the different slags in the cementitious formulations. Mechanical compressive and splitting test determine the mechanical strength of the formulations.
The two slags from steel mills are reactive, show quick setting (due to their abundance in mayenite), and thus they need the addition of GBBS and gypsum to slow down their reactivity.
The slag from the foundry process is not much reactive, it does not have problems of quick setting and expansive reactions and it can be mixed to the cement as it is, without the addition of GBBS.
By choosing the correct quantity of slag, GBBS and gypsum mixed together in different formulations, these materials can reach mechanical strength classes of 32.5 MPa and 42.5 MPa.